| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
130 |
| Tensile strain at break |
％ |
6 |
| Tensile modulus |
MPa |
9600 |
| Flexural strength |
MPa |
ISO 178 |
195 |
| Flexural modulus |
MPa |
8100 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
21 |
| Tensile strength after moisture absorption |
MPa |
ISO 527-1,2 |
116 |
| Tensile modulus after moisture absorption |
MPa |
8200 |
| Tensile strain at break after moisture absorption |
% |
7 |
| Flexural strength after moisture absorption |
MPa |
ISO 178 |
172 |
| Flexural modulus after moisture absorption |
MPa |
6700 |
| Charpy notched impact strength after moisture absorption |
J/m |
ISO 179-1/1eU |
22 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039 |
110 |
| M.Scale |
70 |
| R.Scale(After Moisture absorption) |
103 |
| M.Scale(After Moisture absorption) |
58 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
175～181 |
| Temperature of deflection under load |
0.45 MPa |
℃ |
ISO 75-1,2 |
177 |
| 1.8 MPa |
165 |
| Coefficient of linear thermal expansion |
x10-5/K |
ISO 11359-2 |
2.5 |
| Electrical property |
| Volume resistivity |
Ω・cm |
IEC 60093 |
106 |
| Molding property |
| Mold shrinkage |
MD |
％ |
ISO 294-4 |
0.1 |
| TD |
0.6 |
| Other property |
| Density |
g/cm3 |
ISO 1183 |
1.16 |
| Water absorption |
equilibrium |
％ |
UBE method |
0.6 |