| Mechanical property |
| Tensile strength |
MPa |
ISO 527-1,2 |
80 |
| Tensile strain at break |
％ |
3 |
| Tensile modulus |
MPa |
6200 |
| Flexural strength |
MPa |
ISO 178 |
125 |
| Flexural modulus |
MPa |
6000 |
| Charpy notched impact strength |
kJ/m2 |
ISO 179-1/1eA |
3 |
| Tensile strength after moisture absorption |
MPa |
ISO 527-1,2 |
36 |
| Tensile modulus after moisture absorption |
MPa |
3100 |
| Tensile strain at break after moisture absorption |
% |
4 |
| Flexural strength after moisture absorption |
MPa |
ISO 178 |
51 |
| Flexural modulus after moisture absorption |
MPa |
2100 |
| Rockwell hardness |
R.Scale |
- |
ISO 2039 |
115 |
| M.Scale |
75 |
| R.Scale(After Moisture absorption) |
79 |
| M.Scale(After Moisture absorption) |
14 |
| Thermal property |
| Melting temperature |
℃ |
ISO 11357 |
215～225 |
| Temperature of deflection under load |
1.8 MPa |
℃ |
ISO 75-1,2 |
100 |
| Other property |
| Water absorption |
equilibrium |
％ |
UBE method |
2.0 |